两相黄铜（从H63至H59），合金组织中除了具有塑性良好的α相外，还出现了由电子化合物CuZn为基的β固溶体。β相在高温下具有很高的塑性，而低温下的β′相（有序固溶体）性质硬脆。故(α+β)黄铜应在热态下进行锻造。含锌量大于46%～50%的β黄铜因性能硬脆，不能进行压力加工。

力学性能

LM’s comparison list between different

norms from Copper alloys

Please read below on the wished for trade-name in the left hand column, and get it translated into LM-language on the right-hand

column. The right hand column with our name is either identical in composition or a fully replaceable alloy with only minor differences.

The column in the middle states the norm and its country of origin.

With no marks in front of LM’s alloy = alloy is identical, with this sign “~” = alloy is very similar, fully replaceable.

Product name Country of origin LM’s trade name by or order/inquiry

Cu Sn6  German standard / DIN 17662, Zinnbronzen  Cu Sn6, CW452K

Cu Sn8, Cu Sn8 P  German standard / DIN 17662, Zinnbronzen  Cu Sn8, CW453K, Cu Sn8 P, CW459K

Cu Sn4 Pb4 Zn4  German standard / DIN 17662, Zinnbronzen  Cu Sn4 Pb4 Zn4, CW456K

Cu Ni12 Zn24  German std. / DIN 17663, Kupfer-Nickel (Neusilber)  SS 5243 (nysilver), viss tillg nglighet

黄铜中由于含锌量不同，机械性能也不一样，黄铜的机械性能随含锌量不同而变化。对于α黄铜，随着含锌量的增多，σb和δ均不断增高。对于(α+β)黄铜，当含锌量增加到约为45%之前，室温强度不断提高。若再进一步增加含锌量，则由于合金组织中出现了脆性更大的r相（以Cu5Zn8化合物为基的固溶体），强度急剧降低。（α+β）黄铜的室温塑性则始终随含锌量的增加而降低。所以含锌量超过45%的铜锌合金无实用价值。

普通黄铜的用途很为广泛如水箱带、供排水管、奖章、波纹管、蛇形管、冷凝管、 壳及各种形状复杂的冲制品、小五金件等。随着锌含量的增加从H63到H59，它们均能很好地承受热态加工，多用于机械及电器的各种零件、冲压件及乐器等处。

为了提高黄铜的耐蚀性、强度、硬度和切削性等，在铜-锌合金中加入少量（一般为1%～2%，少数达3%～4%，很个别的达5%～6%）锡、铝、锰、铁、硅、镍、铅等元素，构成三元、四元、甚至五元合金，即为复杂黄铜，亦称特殊黄铜。