C18080-R540 C18080-TR08机械性能铜合金

UNI-BS Pb10  Italian standard / UNI 7013-72  SS 5640-15 (Cu Pb10 Sn10), CC495K

UNI-BS Pb15  Italian standard / UNI 7013-72  Cu Pb15 Sn (Cu Sn7 Pb15-C), CC496K

UNI-BS Pb20  Italian standard / UNI 7013-72  Cu Pb20 Sn (Cu Sn5 Pb20-C), CC497K

CAC304 (HBsC4)  Japanese standard, JIS SS 5234 (Cu Zn25 Al 5, SoMsF75), CC762S

CAC402 (BC2)  Japanese standard, JIS Rg7 (Cu Sn7 Zn4 Pb7), CC493K

CAC406 (BC6)  Japanese standard, JIS SS 5204-15 (Cu Sn5 Pb5 Zn5), CC491K

CAC502B (PBC2B2)  Japanese standard, JIS SS 5465-15 (Cu Sn12), CC483K

CAC702B (AlBC2)  Japanese standard, JIS AB-200, C954, Ampco 18

CAC703 (AlBC3)  Japanese standard, JIS SS 5716-15, SS 5716-20 (Cu Al10 Ni5 Fe4

C1020  Japanese standard, JIS Cu-OF, Cu-SF

C1100  Japanese standard, JIS Cu-ETP (E-Cu 58)

预热和层间温度一般不应超过150℃。焊接铝含量为10%～13%的铝青铜，厚工件推荐预热和层间温度约260℃，焊件宜快速冷却。采用直流反接，短弧和窄焊道施焊。多层焊时层间必须彻底清渣。

普通性能

紫铜是比较纯净的一种铜，一般可近似认为是纯铜，导电性、塑性都较好，但强度、硬度较差一些。紫铜具有优良的导热性﹑延展性和耐蚀性。紫铜中的微量杂质对铜的导电、导热性能有严重影响。其中钛、磷、铁、硅等显著降低电导率,而镉、锌等则影响很小。硫、硒、碲等在铜中的固溶度很小,可与铜生成脆性化合物,对导电性影响不大，但能降低加工塑性。

紫铜在大气、海水和某些非氧化性酸（盐酸、稀硫酸）、碱、盐溶液及多种有机酸（醋酸、柠檬酸）中，有良好的耐蚀性，用于化学工业。另外，紫铜有良好的焊接性，可经冷、热塑性加工制成各种半成品和成品。20世纪70年代，紫铜的产量超过了其他各类铜合金的总产量。

物理性能